- ABS 1,75 mm(12)
- ABS 2,85 mm(1)
- PLA 1,75 mm(172)
- PLA 1,75 mm matt(25)
- Lightweight PLA (LW-PLA)(8)
- High-Speed PLA(13)
- PLA 2,85 mm(12)
- PETG 1,75 mm(88)
- PETG 1,75 mm matt(17)
- PETG 2,85 mm(3)
- SILK(27)
- ASA 1,75 mm(19)
- Nylon (PA)(43)
- PC (Polycarbon.) 1,75 mm(26)
- PC (Polycarbon.) 2,85 mm(4)
- Flexible filaments (TPU) 1,75 mm(39)
- Flexible filaments (TPU) 2,85 mm(4)
- PCTG(1)
- HIPS 1,75 mm(0)
- HIPS 2,85 mm(1)
- PVA(2)
- PP (Polypropylen)(9)
- PMMA(1)
- POM(4)
- CoPE(5)
- Supporting filaments(6)
- Technical filaments(81)
- Medical filaments(10)
- Filaments with graphene(1)
- Filament for 3D pen(3)
- PolyMax PLA 1,75 mm(10)
- PolyMax PLA 2,85 mm(4)
- PolyTerra PLA(24)
- PolyMax PET(0)
- PolyFlex 90A 1,75 mm(5)
- PolyFlex 95A 1,75 mm(8)
- PolyLite Silk PLA 1,75 mm(5)
- PolyLite / PolyPlus PLA 1,75 mm(27)
- PolyLite Pro PLA 1,75 mm(4)
- PolyPlus PLA 2,85 mm(5)
- PolyWood(1)
- Filaments with wood fibres(9)
- Filaments imitating marble(3)
- PoroLay(5)
- MoldLay(1)
- Accessories(27)
- Sale(4)
- News link
- Promotions link
€48.78
Regular price:
€55.43
€39.66
Regular price:
€45.06
€48.78
Regular price:
€55.43
€39.66
Regular price:
€45.06
€48.78
Regular price:
€55.43
€39.66
Regular price:
€45.06
Polymaker PC-ABS filament 1,75 mm, white, 1 kg
Regular price:
Regular price:
product unavailable
add to wishlist
Description
3D printing filament Polymaker PC-ABS is a PC/ABS polymer blend that offers excellent toughness and heat resistance while displaying a good surface finish and good compatibility with metal plating. Models printed with Polymaker PC-ABS filament are designed for applications requiring high deflection temperature under load and high strength at low and high temperatures.
Nozzle Temperature:
250˚C – 270˚C
Printing Speed:
30 – 50mm/s
Bed Temperature:
90˚C – 105˚C
Chamber Temperature:
90˚C – 100˚C
Young’s Modulus:
1832 ± 65 (MPa)
Tensile Strength:
39.9 ± 1.0 (MPa)
Bending Strength:
66.3 ± 1.3 (MPa)
Charpy Impact Strength:
25.8 ± 1.4 (kJ/m2)
When printing with Polymaker™ PC-ABS it is recommended to use a heated chamber.
It is recommended to anneal the printed part right after the printing process to release the residual internal stress when not using a heated chamber.
Annealing settings: 90˚C for 2h.